Phenolic Epoxy Resin Litlhaloso tsa Teknoloji | Mokhoa oa ho paka | Kopo | |||||||||||||
Mohlala | Mmala | Sebopeho | Litaba tse Tiileng (%) | EEW (g/eq) | Softening Ntlha (℃) | Chromaticity (G/H) | Viscosity (mPa·s) | Hydrolyzable Chlorine (ppm) | Litaba tsa Bromine (%) | Likahare tsa Phosphorus (%) | Mohlala | ||||
Phenolic Epoxy Resin | BNE Bisphenol Ke phenol formaldehyde | EMTE200 | Ha e na 'Mala ho ea ho Bosehla bo Khanyang | Tiileng | - | 200-220 | 62-68 | G<2 | - | ≤200 | - | ![]() | Mokotla oa pampiri o nang le PE liner e ka hare: 25 kg / mokotla. | Li-laminate tsa elektronike tsa koporo, li-laminate tsa elektronike, li-adhesive tse thibelang mocheso, lisebelisoa tse kopantsoeng, liphahlo tse hanyetsanang le mocheso o phahameng, boenjiniere ba sechaba le li-inks tsa elektroniki, joalo-joalo. | |
EMTE200H | 190-220 | 65-75 | G≤3 | - | ≤200 | - | |||||||||
EMTE 200A80 | Mokelikeli | 80±1.0 | 190-220 | - | G≤2 | 1100-180 | ≤200 | ![]() | Moropa oa tšepe: 220kg / moropa | ||||||
PNE phenol novolac epoxy resin | EMTE625 | Ha e na 'Mala ho ea ho Bosehla bo Khanyang | Mokelikeli | - | 164-177 | - | G≤1 | 9000-13000 | ≤300 | - | Moropa oa tšepe: 220kg / moropa | Li-laminate tsa elektronike tsa koporo, li-laminate tsa elektronike, li-adhesive tse thibelang mocheso, lisebelisoa tse kopantsoeng, liphahlo tse hanyetsanang le mocheso o phahameng, boenjiniere ba sechaba le li-inks tsa elektroniki, joalo-joalo. | |||
EMTE636 | 170-173 | 28-30 | G≤0.8 | - | ≤200 | ![]() | |||||||||
EMTE636L | 169-173 | 23-27 | G≤1 | ≤300 | - | ||||||||||
EMTE637 | 170-174 | 31-36 | G≤0.8 | ≤250 | - | ||||||||||
EMTE 638A80 | 170-180 | 80±1 | G≤0.8 | 100-280 | ≤200 | - | |||||||||
EMTE638 | 171-175 | 36-40 | G≤0.5 (0.6) | 35-39 | 80-180 | ![]() | |||||||||
EMTE638S | 171-175 | 31-35 | G≤0.5 | - | ≤200 | - | |||||||||
EMTE639 | 174-180 | 44-50 | G≤1 | ≤300 | - | ||||||||||
CNE o-Cresol aldehyde Epoxy resin | EMTE701 | Ha e na 'Mala ho ea ho Bosehla bo Khanyang | Tiileng | 196-206 | 65-70 | G<2 | 500 | - | Mokotla oa pampiri o nang le PE liner e ka hare: 25 kg / mokotla. | Li-laminate tsa elektronike tsa koporo, li-laminate tsa elektronike, li-adhesive tse thibelang mocheso, lisebelisoa tse kopantsoeng, liphahlo tse hanyetsanang le mocheso o phahameng, boenjiniere ba sechaba le li-inks tsa elektroniki, joalo-joalo. | |||||
EMTE702 | 197-207 | 70-76 | G<2 | 500 | - | ||||||||||
EMTE704 | 200-215 | 88-93 | G<2 | <1000 | - | ||||||||||
EMTE704M | 200-215 | 87±1 | G<2 | 40-100 | ![]() | ||||||||||
EMTE704ML | 200-210 | 80-85 | G<2 | <1000 | - | ||||||||||
EMTE704L | 207-215 | 78-83 | G<2 | <1000 | - |