Filimi ea poliester ea primer
Kopo
● Filimi ea primer e sa fetoheng - Letoto la YM3
| Sehlopha | Yuniti | YM30 | YM30A | YM30B | YM31 | YM31A | |||||||
| 'Mala oa Bokaholimo | — | Putsoa | Ha e na 'mala | Molora o motsho | Putsoa | Ha e na 'mala | |||||||
| Botenya | μm | 38 | 50 | 75 | 38 | 50 | 50 | 50 | 75 | 100 | 38 | 50 | |
| Matla a tšepe | MD | MPa | 225 | 220 | 175 | 254 | 232 | 220 | 246 | 244 | 224 | 228 | 232 |
| TD | MPa | 245 | 244 | 235 | 294 | 240 | 244 | 279 | 257 | 247 | 269 | 240 | |
| Ho lelefatsa | MD | % | 151 | 148 | 164 | 153 | 143 | 148 | 150 | 157 | 146 | 159 | 153 |
| TD | % | 127 | 135 | 126 | 124 | 140 | 135 | 132 | 137 | 128 | 117 | 126 | |
| Ho fokotseha ha sekhahla (150℃/metsotso e 30) | MD | % | 1.3 | 1.2 | 1.1 | 1.3 | 1.2 | 1.3 | 0.7 | 0.6 | 0.6 | 1.2 | 1.2 |
| TD | % | 0.04 | 0.01 | 0.02 | 0.03 | -0.01 | -0.01 | 0.1 | 0.01 | 0.02 | 0.03 | -0.01 | |
| Phetisetso | % | 90.4 | 90.5 | 90.5 | 93.8 | 92.8 | 90.5 | 90.4 | 90.6 | 90.2 | 90.8 | 90.9 | |
| Molumo | % | 1.89 | 1.94 | 2.35 | 1.97 | 2.4 | 1.94 | 3.02 | 3.63 | 3.72 | 1.95 | 2.4 | |
| Khanyetso ea Bokaholimo | Ω | 105-7 | 108-10 | 105-7 | 105-7 | 108-10 | |||||||
● Filimi ea primer e bonahatsang YM20, filimi ea motheo e koahelang oligomer e tlase YM40 le filimi ea primer e khabisitsoeng ea SCY/SCP Series:
| Sehlopha | Yuniti | YM20/21 | YM40 | SCY22 | SCY32 | SCP13 | |||||
| Botenya | μm | 25 | 38 | 50 | 125 | 30 | 125 | 188 | 50 | ||
| Matla a tšepe | MD | MPa | 165 | 223 | 221 | 224 | 194 | 179 | 190 | 246 | |
| TD | MPa | 221 | 314 | 234 | 242 | 239 | 206 | 223 | 279 | ||
| Ho lelefatsa | MD | % | 146 | 176 | 165 | 145 | 142 | 179 | 158 | 173 | |
| TD | % | 79 | 133 | 128 | 132 | 106 | 139 | 130 | 138 | ||
| Ho fokotseha ha sekhahla (150℃/metsotso e 30) | MD | % | 1.0 | 1.3 | 1.2 | 1.2 | 1.2 | 1.03 | 1.10 | 1.3 | |
| TD | % | 0 | -0.1 | 0.04 | 0.01 | 0.1 | 0.15 | 0.11 | 0.3 | ||
| Phetisetso | % | 92.1 | 91.6 | 90.2 | 90.3 | 91.1 | 91.7 | 91.7 | 90.9 | ||
| Molumo | % | 2.34/1.3 | 1.38/1.3 | 1.1 | 1.1 | 3.1 | 0.99 | 1 | 1.55 | ||